SPS工艺参数对ZrB2-MoSi2-SiC复合陶瓷组织与高温抗氧化性能的影响
张玉栋1,2, 李继文1, 王南南1,2, 潘昆明2, 张亮亮1,2
1.河南科技大学 材料科学与工程学院,洛阳 471023;
2.金属材料磨损控制与成型技术国家地方联合工程研究中心,洛阳 471003
Effects of SPS process parameters on microstructure and high-temperature oxidation resistance of ZrB2-MoSi2-SiC composite ceramics
ZHANG Yudong1,2, LI Jiwen1, WANG Nannan1,2, PAN Kunming2, ZHANG Liangliang1,2
1. Material Science & Engineering School, Henan University of Science & Technology, Luoyang 471023, China;
2. National Joint Engineering Research Center for Abrasion Control and Molding of Metal Materials, Luoyang 471003, China
全文: PDF (850 KB)   HTML (1 KB) 
输出: BibTeX | EndNote (RIS)      
摘要 采用放电等离子烧结法,在烧结温度为1 700~2 000 ℃,升温速率为75~150 ℃/min,保温3~10 min条件下制备ZrB2-MoSi2-SiC复合陶瓷(ZMS15陶瓷),研究烧结温度、升温速率和保温时间等工艺参数对材料致密度以及1 200 ℃高温抗氧化性能的影响。结果表明:ZrB2-MoSi2-SiC复合陶瓷的致密度随烧结温度升高和升温速率增大而增大,保温时间为7 min时致密度最大。ZMS15陶瓷高温氧化时形成双层结构的氧化层,外层为玻璃态SiO2层,内层为颗粒状富ZrO2层。随烧结温度升高,材料的抗氧化性能增强。ZrB2-MoSi2-SiC复合陶瓷的最佳SPS工艺为烧结温度2 000 ℃、升温速率125 ℃/min、保温时间7 min,所得陶瓷的相对密度大于98.5%,在1 200 ℃氧化72 h后的质量增加率小于8 mg/cm2
服务
把本文推荐给朋友
加入我的书架
加入引用管理器
E-mail Alert
RSS
作者相关文章
张玉栋
李继文
王南南
潘昆明
张亮亮
关键词 放电等离子烧结ZrB2-MoSi2-SiC陶瓷工艺参数相对密度抗氧化性能    
Abstract:ZrB2-MoSi2-SiC composite ceramics (ZMS15 ceramics) were prepared by spark plasma sintering (SPS) at the sintering temperature of 1 700-2 000 ℃, heating rate of 75-150 ℃/min and holding time of 3-10 min. The effects of sintering temperature, heating rate and holding time on the relative density and the oxidation resistance at 1 200 ℃ of the composite ceramics were studied. The results show that the relative density of ZrB2-MoSi2-SiC composite ceramics increases with the increase of sintering temperature and heating rate, and the relative density reaches the maximum value when the holding time is 7 min. ZMS15 ceramic forms a double-layer structure during oxidation. The outer layer is glassy SiO2 layer, and the inner layer is granular ZrO2 layer. With increasing sintering temperature, the high temperture oxidation resistance of the material increases. The optimal SPS process for ZrB2-MoSi2-SiC composite ceramics is sintering temperature of 2 000 ℃, heating rate of 125 ℃/min, and holding time of 7 min. The relative density of the ceramics is greater than 98.5%, and the mass change is less than 8 mg/cm2 after oxidation at 1 200 ℃ for 72 h.
Key wordsspark plasma sintering    ZrB2-MoSi2-SiC ceramic    process parameters    relative density    oxidation resistance
收稿日期: 2020-09-04      出版日期: 2021-01-18
ZTFLH:  TB35  
基金资助:国家自然科学基金资助项目(51901069)
通讯作者: 李继文,教授,博士。电话:13525983980;E-mail: ljwzq@163.com   
引用本文:   
张玉栋, 李继文, 王南南, 潘昆明, 张亮亮. SPS工艺参数对ZrB2-MoSi2-SiC复合陶瓷组织与高温抗氧化性能的影响[J]. 粉末冶金材料科学与工程, 2020, 25(6): 505-512.
ZHANG Yudong, LI Jiwen, WANG Nannan, PAN Kunming, ZHANG Liangliang. Effects of SPS process parameters on microstructure and high-temperature oxidation resistance of ZrB2-MoSi2-SiC composite ceramics. Materials Science and Engineering of Powder Metallurgy, 2020, 25(6): 505-512.
链接本文:  
http://pmbjb.csu.edu.cn/CN/     或     http://pmbjb.csu.edu.cn/CN/Y2020/V25/I6/505
版权所有 © 《粉末冶金材料科学与工程》编辑部
地址:长沙市麓山南路中南大学粉末冶金研究院 邮编:410083 电话:0731-88877163 邮箱:pmbjb@csu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn