纳米SiC对Ti(C,N)基金属陶瓷微观组织与性能的影响

摘要
图/表
参考文献
相关文章 (15)

全文: PDF (962 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要以Ti(C,N),WC,Mo₂C,TaC和Cr₂C₃等粉末为主要原料,Co和Ni作为粘结剂,添加0~11%(体积分数)的纳米SiC粉末作为增强相,制备Ti(C,N)基金属陶瓷,研究SiC含量对陶瓷材料显微组织、力学性能和高温抗氧化性能的影响。结果表明,少量SiC不会改变金属陶瓷原有的相结构,而随SiC含量增加,环形相的完整性下降,硬质相的平均晶粒尺寸减小。SiC体积分数为5%的Ti(C,N)基金属陶瓷综合性能较优异,硬度(HRA)为88.8,抗弯强度为2 280 MPa,断裂韧性为13.22×10³kN·m^-3/2。添加SiC可增强Ti(C,N)基金属陶瓷的高温抗氧化性能,氧化后材料表面生成致密的SiO₂膜层。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	龚涤凡
	李詠侠
	杨海林
	邹丹
	刘艳军

关键词 ： Ti(C,N)基金属陶瓷, 纳米SiC, 微观组织, 力学性能, 高温抗氧化性能

Abstract：Ti(C,N), WC, Mo₂C, TaC and Cr₂C₃powders were used as the main raw materials, Co and Ni powders were used as binders, and nano-SiC powders with 0-11% volume fraction were added as the reinforcing phase to prepare Ti- (C,N) based cermets. The effect of SiC content on the microstructure, mechanical properties and high temperature oxidation resistance of ceramic materials was studied. The results indicated that a small amount of SiC could not change the original phase structure of the cermet. As SiC content increased, the integrity of the ring phase decreased and the average grain size of the hard phase reduced. Ti(C,N)-based cermet with 5% volume fraction SiC had excellent comprehensive properties, with Rockwell hardness of 88.8 HRA, flexural strength of 2 280 MPa, and fracture toughness of 13.22×10³ kN∙m^-3/2. The addition of SiC enhanced the high temperature oxidation resistance of Ti(C,N) based cermets and produced a dense SiO₂ film on the surface.

Key words： Ti(C,N)-based cermets nano-SiC microstructure mechanical properties high temperature oxidation resistance

收稿日期: 2020-05-13 出版日期: 2020-09-18

ZTFLH:

TG148

通讯作者: 杨海林,副教授,博士。电话：13973182703;E-mail: y-hailin@csu.edu.cn

引用本文:

龚涤凡, 李詠侠, 杨海林, 邹丹, 刘艳军. 纳米SiC对Ti(C,N)基金属陶瓷微观组织与性能的影响[J]. 粉末冶金材料科学与工程, 2020, 25(4): 321-329.
GONG Difan, LI Yongxia, YANG Hailin, ZOU Dan, LIU Yanjun. Nano-SiC addition on microstructure, mechanical properties and high temperature oxidation resistance of Ti(C,N)-based cermets. Materials Science and Engineering of Powder Metallurgy, 2020, 25(4): 321-329.

链接本文:

http://pmbjb.csu.edu.cn/CN/ 或 http://pmbjb.csu.edu.cn/CN/Y2020/V25/I4/321

[1] BHAUMIK S K, BALASUBRAMANIAM R, UPADHYAYA G S, et al.Oxidation behaviour of hard and binder phase modified WC-10Co cemented carbides[J]. Journal of Materials Science Letters, 1992, 11(21): 1457-1459.
[2] LOFAJ F, KAGANOVSKII Y S.Kinetcs of WC-Co oxidation accompanied by swelling[J]. Journal of Materials Science, 1995, 30(7): 1811-1817.
[3] BASU S N, SARIN V K.Oxidation behavior of WC-Co[J]. Materials Science and Engineering A, 1996, 209(1/2): 206-212.
[4] VOITOVICH V B, SVERDEL V V, VOITOVICH R F, et al.Oxidation of WC-Co, WC-Ni and WC-Co-Ni hard metals in the temperature range 500-800 ℃[J]. International Journal of Refractory Metals and Hard Materials, 1996, 14(4): 289-295.
[5] ETTMAYER P, KOLASKA H, LENGAUER W, et al.Ti(C,N) cermets-metallurgy and properties[J]. International Journal of Refractory Metals and Hard Materials, 1995, 13(6): 343-351.
[6] BOLOGNINI S, FEUSIER G, MARI D, et al.High temperature mechanical behavior of Ti(C,N)-Mo-Co cermets[J]. International Journal of Refractory Metals and Hard Materials, 1998, 16(4/6): 257-268.
[7] MARI D, BOLOGNINI S, FEUSIER G, et al.TiMoCN based cermets: Part I. Morphology and phase composition[J]. International Journal of Refractory Metals and Hard Materials, 2003, 21(1/2): 37-46.
[8] MARI D, BOLOGNINI S, FEUSIER G, et al.TiMoCN based cermets Part II. Microstructure and room temperature mechanical properties[J]. International Journal of Refractory Metals and Hard Materials, 2003, 21(1/2): 47-53.
[9] SHI Z M, YIN D Z, ZHANG D Y, et al.Characterisation of Ti(C,N)-based cermets with various nitrogen contents studied by EBSD/SEM and TEM[J]. Journal of Alloys and Compounds, 2017, 695: 2857-2864.
[10] ZHANG M, YANG Q Q, XIONG W H, et al.Effect of Mo and C additions on magnetic properties of TiC-TiN-Ni cermets[J]. Journal of Alloys and Compounds, 2015, 650(2): 700-704.
[11] PARK J K, PARK S T.Densification of TiN-Ni cermet swith addition of Mo₂C[J]. International Journal of Refractory Metals and Hard Materials, 1999, 17(1): 295-298.
[12] ETTMAYER P, LENGAUER W.The history of Ti(C,N) cermets[J]. Powder Metallurgy International, 1989, 21(2): 37-38.
[13] ZHANG X, LIU N, RONG C.Effect of molybdenum content on the microstructure and mechanical properties of ultra-fine Ti (C,N) based cermets[J]. Mater Charact, 2008, 59(4): 1690-1696.
[14] ROLANDER U, WEINL G, ZWINKELS M, Effect of Ta on structure and mechanical properties of (Ti,Ta,W)(C,N)-Co cermets[J]. International Journal of Refractory Metals and Hard Materials, 2001,19(2): 325-328.
[15] YOSHIMURA H, SUGIZAWA J, NISHIGAKI K.The reactior occuring during sintering and the characteristics of TiC-20%TiN- 15%WC-10%TaC-9%Mo-5.5%Ni-11%Co cermet[J]. Trend Refract Met Hard Met Spec Mater Technol, 1981(2): 727-741.
[16] PARK D S, PARK C, LEE Y D.Oxidation of Ti(C,N)-based ceramics exposed at 1 373 K in air[J]. J Am Ceram Soc, 2000, 83(3): 672-674.
[17] 郑勇, 刘文俊, 游敏, 等. Cr₃C₂和VC对Ti(C,N)基金属陶瓷中环形相的价电子结构和性能的影响[J]. 硅酸盐学报, 2004, 32(4): 422-428.
ZHENG Yong, LIU Wenjun, YOU Min, et al.Effects of Cr₃C₂ and VC on the valence electron structure and properties of the ring-shaped phase in Ti(C,N)-based cermets[J]. Journal of The Chinese Ceramic Society, 2004, 32(4): 422-428.
[18] HUANG S G, LI L, BIEST O V D, et al. VC-and Cr₃C₂-doped WC-NbC-Co hardmetals[J]. Journal of Alloys and Compounds, 2008, 464(2): 205-211.
[19] LEI Y W, SUN J, DU X W, et al.Properties and microstructure of VC/Cr₃C₂-doped WC/Co cemented carbides[J]. Rare Metal, 2007, 26(6): 584-590.
[20] 薛萍, 张建军, 艾云龙, 等. SiC掺杂WC-10Ni硬质合金的真空烧结及性能[J], 稀有金属材料与工程, 2019, 48(2): 566-572.
XUE Ping, ZHANG Jianjun, AI Yunlong, et al.Vacuum sintering and properties of SiC-doped WC-10Ni cemented carbide[J]. Rare Metal Materials and Engineering, 2019, 48(2): 566-572.
[21] SUN L, PAN J S.Fabrication and characterization of TiC_w/ MoSi₂ and SiC_w/MoSi₂ composites[J]. Materials Letter, 2002, 52(2): 223-228.
[22] LI C W, HUANG Y, WANG C A.Mechanical properties and microstructure of laminated Si₃N₄+SiC_w/BN+Al₂O₃ ceramics densified by spark plasma sintering[J]. Materials Letter, 2002, 57(1): 336-342.
[23] ZHANG X N, GENG L, XU B.Compressive behaviour of Al-based hybrid composites reinforced with SiC whiskers and SiC nanoparticles[J]. Materials Chemisty and Physics, 2007, 101(1): 242-246.
[24] WU P, ZHENG Y, ZHAO Y L, et al.Effect of SiC whisker addition on the microstructures and mechanical properties of Ti(C,N)-based cermets[J]. Materials & Design, 2011, 32(2): 951-956.
[25] PENG Y, PENG Z J, REN X Y, et al.Effect of SiC nano-whisker addition on TiCN-based cermets prepared by spark plasma sintering[J]. International Journal of Refractory Metals and Hard Materials, 2012, 34: 36-40.
[26] SCHUBERT W D, NEUMEISTER H, KINGER G, et al.Hardness to toughness relationship of fine-grained WC-Co hardmetals[J]. International Journal of Refractory Metals and Hard Materials, 1998, 16(2): 133-142.
[27] MASSALSKI T B, OKAMOTO H.Binary Alloy Phase Diagrams, Vol. 3[M]. OH, USA: ASM International, Materials Park, 1990.
[28] 陈丽勇. WC-Co硬质合金的氧化及磨损[D]. 长沙: 中南大学, 2016.
CHEN Liyong.Oxidation and wear of WC-Co cemented carbide[D]. Changsha: Central South University, 2016.
[29] ZHOU S B, Ablation behavior of ZrB₂-SiC-ZrO₂ ceramic composites by means of the oxyacetylene torch[J]. Corrosion Science, 2009, 51(9): 2071-2079.
[30] CHU Y, LI H, FU Q, et al.Nanowire-toughened SiC coating for oxidation protection of C/C composites[J]. Corrosion Science, 2013, 70(1): 11-16.