优化钢铁热轧精轧前除磷箱的构造
赵胜利
上海梅山钢铁股份有限公司,南京 210039
Optimized hot rolling descaling box structure before finishing rolling
ZHAO Shengli
Shanghai Meishan Iron and Steel Co., Ltd, Nanjing 210039, China
摘要 精轧前除磷(即去除粗轧后板坯表面的氧化铁皮)是钢铁热轧轧线的关键环节。针对目前普遍采用的高压水喷射除磷所存在的除磷箱框架整体薄弱及夹送辊牌坊出现变形导致夹送辊运行不畅且拆装困难,除磷箱本体立柱及牌坊部位受高压水冲刷出现凹槽及腐蚀严重,夹送辊油缸设计不合理导致故障率高,以及除磷辊传动机构标高不一致等问题,本文作者对精轧除磷箱整体结构及布局进行优化,将夹送辊牌坊设计成U型结构并增加强度来保证夹送辊运行稳定,对除磷箱本体易冲刷部位增加防护衬板、优化夹送辊油缸的安装连接方式从而降低油缸故障率,整体优化除磷箱夹送辊、除磷辊、气动液压装置等液压润滑系统和增加辊道冷却等改进措施,提高精轧前除磷箱的整体功能和性能,满足现场生产需求,提升产品质量。
关键词 :
除磷箱 ,
牌坊 ,
本体 ,
夹送辊油缸 ,
强度 ,
结构 ,
润滑
Abstract :Phosphorus removal before finish rolling (remove the oxide iron on the surface of the slab after rough rolling) is the key equipment of hot rolling line. In view of the weakness of the frame of the phosphorus removal box and the deformation of the pinch roll arch existing in the high-pressure water jet phosphorus removal, the operation of the pinch roll is not smooth and the disassembly and assembly is difficult, the main column and archway of the phosphorus removal box are grooved and corroded by high pressure water, the unreasonable design of the roller cylinder resulted in a high failure rate, and the inconsistent elevation of the phosphorus removal roller transmission mechanism. In this paper, optimizing the overall structure and layout of the dephosphorization box in finishing rolling, using the U-shaped structure and increasing the strength of the pinch roll arch to ensure the stable operation of the pinch roll, adding the protective lining plate to the parts easy to be washed out of the dephosphorization box body, optimizing the installation and connection mode of the pinch roll oil cylinder, so as to reduce the failure rate of the oil cylinder. Optimize the hydraulic lubrication system such as pinch roll, dephosphorization roll and pneumatic hydraulic device of dephosphorization tank as a whole and increase the cooling of roller table and other improvement measures, improve the overall function and performance of dephosphorization tank before finishing rolling, meet the production demand on site and improve the product quality.
Key words :
phosphorus removal box
archway
body
pinch roller cylinder
strength
structure
lubrication
收稿日期: 2019-05-19
出版日期: 2020-06-19
通讯作者:
赵胜利,工程师。电话:17761740878;E-mail: 254716894@qq.com
[1] 孙志礼, 冷兴聚, 魏严刚, 等. 机械设计[M]. 沈阳: 东北大学出版社, 2000: 87-88. SUN Zhili, LENG Xingju, WEI Yangang, et al.Mechanical Design[M]. Shenyang: Northeast University Press, 2000: 87-88. [2] 刘鸿文. 材料力学[M]. 北京: 高等教育出版社, 1991: 23-24. LIU Hongwen.Mechanics of Materials[M]. Beijing: Higher Education Press, 1991: 23-24. [3] 哈尔滨工业大学理论力学教研组. 理论力学[M]. 北京: 高等教育出版社, 1997: 35-36 . Teaching and Research Group of Theoretical Mechanics, Harbin University of Technology. Theoretical Mechanics[M]. Beijing: Higher Education Press, 1997: 35-36. [4] 东北工学院《机械零件设计手册》编写组. 机械零件设计手册/中册[M]. 第2版. 北京: 冶金工业出版社, 1982: 68-70. Compilation Group of Mechanical Parts Design Manual of Northeast Institute of Technology. Mechanical Parts Design Manual/Medium Book[M]. 2nd ed. Beijing: Metallurgical Industry Press, 1982: 68-70. [5] 王国栋. 中国中厚板轧制技术与装备[M]. 北京: 冶金工业出版社, 2009: 8-9. WANG Guodong.China Medium and Heavy Plate Rolling Technology and Equipment[M]. Beijing: Metallurgical Industry Press, 2009: 8-9. [6] 孙桓, 陈作模. 机械原理[M]. 北京: 高等教育出版社, 2000: 33-34. SUN Huan, CHEN Zuomo.Mechanical Principle[M]. Beijing: Higher Education Press, 2000: 33-34. [7] 吴伊蓝. 高压水除鳞技术在热轧带钢生产上的应用田[J]. 浙江冶金, 2002(4): 012. WU Yilan.Application field of high-pressure water descaling technology in hot-rolled strip production[J]. Zhejiang Metallurgy, 2002(4): 012. [8] 夏先平, 孙业中. 精轧区热轧带钢表面氧化铁皮缺陷成因与预防明[J]. 轧钢, 2002, 19(3): 9-12. XIA Xianping, SUN Yezhong.Causes and prevention of iron oxide scale defects on hot rolled strip surface in finishing rolling area[J]. Rolling, 2002, 19(3): 9-12. [9] 卢晓江, 何迎春, 赖维. 高压水射流清洗技术及应用[M]. 北京: 化学工业出版社, 2006: 63-64. LU Xiaojiang, HE Yingchun, LAI Wei.High-Pressure Water Jet Cleaning Technology and Application[M]. Beijing: Chemical Industry Press, 2006: 63-64. [10] 薛念福, 李里, 陈继林, 等. 热轧带钢除鳞技术研究[J]. 钢铁钒钛, 2003, 24(3): 52-59. XUE Nianfu, LI Li, CHEN Jilin, et al.Study on descaling technology of hot rolled strip[J]. Vanadium and Titanium, 2003, 24(3): 52-59. [11] 赵宗波. 现代热轧带钢除鳞技术川[J]. 轧钢, 1993, 10(4): 28-28. ZHAO Zongbo.Modern hot strip descaling technology Chuan[J]. Rolling, 1993, 10(4): 28-28. [12] 吴祝民. 热· 带· 氧化铁皮的成因及对策[J]. 轧钢, 2007, 24(3): 22-23. WU Zhumin.Hot belt causes and countermeasures of oxide scale[J]. Steel Rolling, 2007, 24(3): 22-23. [13] 申明. 高压水除磷设备故障分析与处理[J]. 轻工设计, 2011, 4(2): 13-14. SHEN Ming.Fault analysis and treatment of high-pressure water phosphorus removal equipment[J]. Light Industry Design, 2011, 4(2): 13-14. [14] 肖鹏, 崔晓嘉, 徐良, 等. 浅谈板带钢的高精度轧制技术[J].河北冶金, 2012, 2(3): 2-3. XIAO Peng, CUI Xiaojia, XU Liang, et al.Talking about high precision rolling technology of plate and strip steel[J]. Hebei Metallurgy, 2012, 2(3): 2-3. [15] 中村, 王怀宇. 板坯加热时氧化铁皮的高温剥离性[J]. 宽厚板, 1997, 6(2): 15-16. ZHONG Cun, WANG Huaiyu.High temperature peeling property of oxide scale when slab is heated[J]. Heavy Plate, 1997, 6(2): 15-16.
[1]
易君, 张贝, 汤振霄, 向秋玲, 易茂中. 熔渗法制备MoSi2 改性C/C复合材料的组织结构与力学性能 [J]. 粉末冶金材料科学与工程, 2019, 24(6): 529-535.
[2]
鲁欣欣, 刘伟, 李林, 李建斌. MgO-Y2 O3 -Re2 O3 添加对氮化硅陶瓷微观组织及性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(6): 536-541.
[3]
卢洋, 赵哲, 明亮, 胡子健, 薛翔远, 邓欣, 刘建业, 戚文君, 牛留辉, 高文华. 选区激光熔化成形工艺参数对Fe20Cr5Al合金致密度和力学性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(5): 422-429.
[4]
邱天旭, 张继峰, 孙露, 万霖, 申小平. 粉末冶金Fe-5(Cu-10Sn)-石墨-P-MoS2 含油材料的摩擦性能 [J]. 粉末冶金材料科学与工程, 2019, 24(5): 459-466.
[5]
邓彪, 周科朝, 肖和, 魏秋平, 马莉, 易铭昆, 罗一杰, 李亮. 微观结构对纳米金刚石涂层WC-Co结合性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(4): 358-364.
[6]
龙翔宇, 雷霆, 王坤婵, 詹振翔. 以HKUST-1为前驱体的Cu@Pt/C催化剂的结构及对甲醇的催化氧化性能研究 [J]. 粉末冶金材料科学与工程, 2019, 24(3): 289-295.
[7]
刘羽祚, 李喜德, 李菊英, 裴后昌, 杨军胜, 贺跃辉. 造孔剂(NH4 )2 CO3 和尿素含量对TiAl 多孔材料性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(3): 255-260.
[8]
孙晔华, 李国栋, 叶国柱, 史琦, 张洋, 何岸青. 炭纤维涂层改性对快速制备Cf /SiC复合材料力学性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(3): 248-254.
[9]
苏逸斯, 冯波, 胡晓明, 刘培海, 李光强, 樊希安. Ba-Pb双掺杂与晶粒细化的协同调整对BiCuSeO半导体陶瓷热电性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(3): 239-247.
[10]
李全, 刘祖铭, 彭凯, 赵凡, 吕学谦. 机械球磨Y2 O3 粉末的组织结构演变 [J]. 粉末冶金材料科学与工程, 2019, 24(3): 226-231.
[11]
伏利, 黄欢欢, 陈小明, 刘伟, 赵坚, 张磊, 周夏凉. 多次激光熔覆工艺对铁基合金涂层组织和性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(2): 95-99.
[12]
徐一溪, 杨丰豪, 王喜云, 易茂中. 热处理对PAN基炭纤维微观结构和力学性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(2): 147-153.
[13]
刘咸超, 郭容. Al2 O3 基复合金属陶瓷模具材料的组织结构与力学性能 [J]. 粉末冶金材料科学与工程, 2019, 24(1): 58-62.
[14]
曾晗, 吴宏, 周承商, 刘咏, 刘彬. 烧结温度对高速钢颗粒增强钛基复合材料组织与性能的影响 [J]. 粉末冶金材料科学与工程, 2019, 24(1): 68-74.
[15]
伏利, 陈小明, 马红海, 刘伟, 孟金博. 爆炸喷涂制备流体机械抗冲蚀涂层的性能 [J]. 粉末冶金材料科学与工程, 2019, 24(1): 75-79.