Diffusion behavior of FCC Ni-Al system in spark plasma sintering electric field
WANG Fei1, LIU Yuling1, DU Changfa2, MIN Qianhui1, LIU Huixin1, WEN Shiyi1, DU Yong1
1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China; 2. School of Mathematics and Statistics, Central South University, Changsha 410083, China
Abstract：The smelting method was employed to prepare the Ni-9Al (mole fraction, %) alloys and pure Ni, and then the Ni/Ni-Al/Ni diffusion couples were annealed for diffusion in spark plasma sintering (SPS). The concentration profiles of FCC Ni-Al system at 1 173-1 373 K under the effect of SPS current were obtained combining with electronic probe microanalysis (EPMA). The Sauer-Freise method and empirical formula were employed to calculated diffusion coefficients respectively. The concentration profiles without current were simulated based on the atomic mobilitiy parameters without the influence of applied field and then the diffusion coefficients were calculated meanwhile. Comparing the simulated concentration profiles with the experimental ones. The results show that the current promotes the diffusion of Ni-Al alloys. The direction of the current has negligible effect on the diffusion of Ni-Al alloys. The concentration profiles and diffusion coefficients under different current directions have a high degree of overlap, indicating that the influence of electromigration on the diffusion of Ni-Al alloy is negligible. The applied current has little effect on the diffusion frequency factor, while the applied current significantly reduces the diffusion activation energy.
王飞, 刘钰玲, 都昌发, 闵倩辉, 刘辉新, 文诗艺, 杜勇. 放电等离子烧结电场下Ni-Al体系FCC相的扩散行为[J]. 粉末冶金材料科学与工程, 2021, 26(5): 412-418.
WANG Fei, LIU Yuling, DU Changfa, MIN Qianhui, LIU Huixin, WEN Shiyi, DU Yong. Diffusion behavior of FCC Ni-Al system in spark plasma sintering electric field. Materials Science and Engineering of Powder Metallurgy, 2021, 26(5): 412-418.
[1] 黄伯云, 韦伟峰, 李松林, 等. 现代粉末冶金材料与技术进展[J]. 中国有色金属学报, 2019, 29(9): 1917-1933. HUANG Boyun, WEI Weifeng, LI Songlin, et al.Modern powder metallurgy materials and technology progress[J]. Chinese Journal of Nonferrous Metals, 2019, 29(9): 1917-1933. [2] LI R D, YUAN T C, LIU X J, et al.Enhanced atomic diffusion of Fe-Al diffusion couple during spark plasma sintering[J]. Scripta Materialia. 2016, 110: 105-108. [3] ARRHENIUS S. Chemical reaction velocities[J]. Zeit Physikal Chem, 1899, 28: 317-335. [4] BLECH I A.Electromigration in thin aluminum films on titanium nitride[J]. Journal of Applied Physics, 1977, 47(4): 1203-1208. [5] GARAY J E, TAMBURINI U A, MUNIR Z A.Enhanced growth of intermetallic phases in the Ni-Ti system by current effects[J]. Acta Materialia, 2003, 51(15): 4487-4495. [6] ZHAO J F, GARAY J E, TAMBURINI U A, et al.Directional electromigration-enhanced interdiffususion in the Cu-Ni system[J]. Journal of Applied Physics, 2007, 102(11): 114902. [7] DENG S H, YUAN T C, LI R D, et al.Influence of electric current on interdiffusion kinetics of W-Ti system during spark plasma sintering[J]. International Journal of Refractory Metals and Hard Materials, 2018, 75: 184-190. [8] DENG S H, LI R D, YUAN T C, et al.The preferential growth behaviors of the intermetallics at the W/Co interface during spark plasma sintering[J]. Applied Physics Letters, 2020, 117(19): 194102. [9] ROGER C R. The Superalloys (Fundamentals and Applications)[M]. London: Cambridge University Press, 2006: 33-120. [10] 王君. 镍基高温合金在航空发动机中的应用[J]. 中国新通信, 2019, 21(1): 221-222. WANG Jun.Application of Nickel-based superalloy in aero- engine[J]. China New Communications, 2019, 21(1): 221-222. [11] SAUER F, FREISE V.Diffusion in binary mixtures with volume change[J]. Z Electrochem, 1962, 66: 352-363. [12] GUILLEMOT F, BOLIVEAU M, BOHN M, et al.On the diffusion in the Mo-Ta refractory system[J]. International Journal of Refractory Metals and Hard Materials, 2001, 19(3): 183-189. [13] DUPIN N, ANSARA I, SUNDMAN B.Thermodynamic re-assessment of the ternary system Al-Cr-Ni[J]. Calphad, 2001, 25(2): 279-298. [14] MIN Q H, LIU Y L, DU Y.Interdiffusion and atomic mobilities in FCC Ag-Mg and Ag-Mn alloys[J]. Calphad, 2019, 65: 93-100. [15] LECHELLE J, NOYAU S, AUFORE L, et al.Volume interdiffusion coefficient and uncertainty assessment for polycrystalline materials, Diffus[J]. Fundam Org, 2012, 17(2): 1-39. [16] JÖNSSON B. Ferromagnetic ordering and diffusion of carbon and nitrogen in bcc Cr-Fe-Ni alloys[J]. Zeitschrift Fur Metallkunde, 1994, 85(7): 498-501. [17] ZHANG L J, DU Y, CHEN Q, et al.Atomic mobilities and diffusivities in the FCC, L12and B2 phases of the Ni-Al system[J]. International Journal of Materials Research, 2010, 101(12): 1461-1475. [18] CHENG K M, LIU D D, ZHANG L J, et al.Interdiffusion and atomic mobility studies in Ni-rich FCC Ni-Al-Mn alloys[J]. Journal of Alloys and Compounds, 2013, 579: 124-131. [19] XU G H, LIU Y J, KANG Z T.Mobilities, interdiffusivities and their kinetic implications for fCC Ni-Al-Nb alloys[J]. Journal of Alloys and Compounds, 2017, 709: 272-276. [20] LIU Y L, ZHANG C, DU C F.CALTPP: a general program to calculate the thermophysical properties[J]. Journal of Material Science & Technology, 2020, 42: 229-240. [21] LIU H X, LIU Y L, DU Y, et al.Atomic mobilities and diffusivities in FCC Co-X (X=Mn, Pt and Re) alloys[J]. Calphad, 2019, 64: 306-312. [22] YANG C, MO D G, LU H Z, et al.Reaction diffusion rate coefficient derivation by isothermal heat treatment in spark plasma sintering system[J]. Scripta Materialia, 2017, 134: 91-94. [23] WATANABE M, HORITA Z, FUJINAMI T, et al. Application of analytical electron microscopy to diffusivity measurement in NiAl System[J]. Defect and Diffusion Forum, 1993, 95/98: 579-586.
2021, Vol. 26 