Abstract:Electrocatalytic nitrogen reduction reaction (eNRR) is considered as an effective strategy for producing $NH_{3}/NH_{4}^{+}$ with low concentrations under environmental conditions, and designing appropriate catalysts is the key to efficiently driving eNRR. This study used a hydrothermal method to prepare MIL-101 catalyst and investigated the effects of hydrothermal temperature and Gd element doping on the eNRR performance of MIL-101 catalyst. The results show that 150-M-101 has the highest crystallinity and eNRR performance (NH3 yield of 11.5 μg/(h·mg), Faraday efficiency of 30.5%). The surface of MIL-101-0.5Gd is concave, exposing the internal rough pore structure, improving the apparent activity of the catalyst. At the same time, the increase of oxygen vacancy concentration optimizes the characteristic activity of the catalyst, the NH3 yield and Faraday efficiency at 0.1 mol/L LiClO4 electrolyte and -1.3 V potential are 16.7 μg/(h·mg) and 37.6%, respectively, which are better than undoped 150-MIL-101. The catalyst also has good long-term stability.
[1] GRUBER N, GALLOWAY J N.An earth-system perspective of the global nitrogen cycle[J]. Nature, 2008, 451: 293-296. [2] ROSCA V, DUCA M, DE GROOT M T, et al. Nitrogen cycle electrocatalysis[J]. Chemical Reviews, 2009, 109(6): 2209-2244. [3] FOSTER S L, PEREZ BAKOVIC S I, DUDA R D, et al. Catalysts for nitrogen reduction to ammonia[J]. Nature Catalysis, 2018, 1(7): 490-500. [4] LI W, FANG W, WU C, et al.Bimetal-MOF nanosheets as efficient bifunctional electrocatalysts for oxygen evolution and nitrogen reduction reaction[J]. Journal of Materials Chemistry A, 2020, 8(7): 3658-3666. [5] HE Y, TAN Q, LU L, et al.Metal-nitrogen-carbon catalysts for oxygen reduction in PEM fuel cells: self-template synthesis approach to enhancing catalytic activity and stability[J]. Electrochemical Energy Reviews, 2019, 2: 231-251. [6] CHEN J G, CROOKS R M, SEEFELDT L C, et al.Beyond fossil fuel-driven nitrogen transformations[J]. Science, 2018, 360: 6391-6611. [7] LI H, SHANG J, AI Z, et al.Efficient visible light nitrogen fixation with BiOBr nanosheets of oxygen vacancies on the exposed {001} facets[J]. Journal of the American Chemical Society, 2015, 137(19): 6393-6399. [8] CHAE H K, SIBERIO-PEREZ D Y, KIM J, et al. A route to high surface area, porosity and inclusion of large molecules in crystals[J]. Nature, 2004, 427: 523-527. [9] ZHAO Z, PARK J, CHOI C, et al.Engineering vacancy and hydrophobicity of two-dimensional TaTe2 for efficient and stable electrocatalytic N2 reduction[J]. Innovation, 2022, 3(1): 100190. [10] CAO N, CHEN Z, ZANG K T, et al.Doping strain induced Bi-Ti3+ pairs for efficient N2 activation and electrocatalytic fixation[J]. Nature Communications, 2019, 10: 2877. [11] HUSSAIN M, LU T, YE C, et al.Role of economic policies, renewable energy consumption, and natural resources to limit carbon emissions in top five polluted economies[J]. Resources Policy, 2023, 83: 103605. [12] MUSHTAQ M A, ARIF M, YASIN G, et al.Recent developments in heterogeneous electrocatalysts for ambient nitrogen reduction to ammonia: activity, challenges, and future perspectives[J]. Renewable and Sustainable Energy Reviews, 2023, 176: 113197. [13] ARIF M, BABAR M, AZHAR U, et al.Rational design and modulation strategies of Mo-based electrocatalysts and photo electrocatalysts towards nitrogen reduction to ammonia (NH3)[J]. Chemical Engineering Journal, 2023, 451: 138320. [14] YANG L, WU T W, ZHANG R, et al.Insights into defective TiO2 in electrocatalytic N2 reduction: combining t-heoretical and experimental studies[J]. Nanoscale, 2019, 11: 1555-1562. [15] LEE H K, KOH C S L, LEE Y H, et al. Favoring the unfavored: selective electrochemical nitrogen fixation using a reticular chemistry approach[J]. Science Advances, 2018, 4(3): eaar3208. [16] ZHAO L, ZHOU J, ZHANG L, et al.Anchoring Au(111) on a bismuth sulfide nanorod: boosting the artificial electrocatalytic nitrogen reduction reaction under ambient conditions[J]. ACS Applied Materials & Interfaces, 2020, 12(50): 55838-55843. [17] CHEN D E, LUO M, NING S, et al.Single-atom gold isolated onto nanoporous MoSe2 for boosting electrochemical nitrogen reduction[J]. Nano Micro Small, 2022, 18: 2104043. [18] DAS A, NAIR A S, MANDAL S C, et al.Current density calculations of an octahedral Fe nanocluster for selective electrocatalytic for nitrogen reduction[J]. ACS Applied Nano Materials, 2021, 4: 7758-7770. [19] JIAO S, FU X, RUAN S, et al.Breaking the periodic arrangement of atoms for the enhanced electrochemical reduction of nitrogen and water oxidatio[J]. Science China Materials, 2022, 65(1): 147-154. [20] WU T W, LI X Y, ZHU X J, et al.P-doped graphene toward enhanced electrocatalytic N2 reduction[J]. Chemical Communications, 2020, 56(12): 1831-1834. [21] XIAO Y, SHEN C, LONG T, et al.Theoretical establishment and screening of an efficient catalyst for N2 electroreduction on two-dimensional transition-metal bborides (MBenes)[J]. Chemical Materials, 2021, 33(11): 4023-4034. [22] SHEN Y, PAN T, WANG L, et al.Programmable logic in metal-organic frameworks for catalysis[J]. Advance Materials, 2021, 33(46): 2007442. [23] ZHAI Z B, YAN W, DONG L, et al.Catalytically active sites of MOF-derived electrocatalysts: synthesis, characterization, theoretical calculations, and functional mechanisms[J]. Journal of Materials Chemistry A, 2021, 9(36): 20320-20344. [24] XIN Z F, WANG Y R, CHEN Y F, et al.Metallocene implanted metalloporphyrin organic framework for highly selective CO2 electroreduction[J]. Nano Energy, 2019, 67: 104233. [25] LV Y, WANG Y Q, YANG M, et al.Nitrogen reduction through confined electro-catalysis with carbon nanotube inserted metal-organic frameworks[J]. Journal of Materials Chemistry A, 2021, 9(3): 1480-1486. [26] WEI Z, FENG Y, MA J, et al.Co-doped graphene edge for enhanced N2-to-NH3 conversion[J]. Journal of Energy Chemistry, 2020, 48(9): 322-327. [27] LI Z N, LIU X M, JIN W, et al.Adsorption behavior of arsenicals on MIL-101(Fe): the role of arsenic chemical structures[J]. Journal of Colloid and Interface Science, 2019, 554: 692-704. [28] JIN Y N, MI X C, QIAN J L, et al.Modular Construction of an MIL-101(Fe)@MIL-100(Fe) dual compartment nanoreactor and its boosted photocatalytic activity toward tetracycline[J]. ACS Applied Materials & Interfaces, 2022, 14(42): 48285-48295. [29] SHI L, YIN Y, WANG S J, et al.Rigorous and reliable operations for electrocatalytic nitrogen reduction[J]. Applied Catalysis B: Environmental, 2020, 278: 119325. [30] BAI Z Q, YUAN L Y, ZHU L, et al.Introduction of amino groups into acid-resistant MOFs for enhanced U(VI) sorption[J]. Journal of Materials Chemistry A, 2015, 3(2): 525-534. [31] SUN X J, XI Q B, ZHAO Z X, et al.Synthesis and adsorption performance of MIL-101(Cr)/graphite oxide composites with high capacities of n-hexane[J]. Chemical Engineering Journal, 2014, 239: 226-232. [32] LU C X, ZHOU Y Z, LI L Z, et al.Conversion of glucose into 5-hydroxymethylfurfural catalyzed by Cr-and Fe-containing mixed-metal metal-organic frameworks[J]. Fuel, 2023, 333: 126415. [33] ZHAO T, ZHU H X, DONG M, et al.Low-temperature and additive-free synthesis of spherical MIL-101(Cr) with enhanced dye adsorption performance[J]. Inorganics, 2022, 10(3): 33. [34] WAN Y C, ZHENG M Y, LV R T, et al.Rational design of Mo2C nanosheets anchored on hierarchically porous carbon for boosting electrocatalytic N2 reduction to NH3[J]. Materials Today Energy, 2022, 32: 101240. [35] JIANG Q S, HAN Z L, QU N, et al.Low-cost magnetic clay derivants from palygorskite/MIL-101(Fe) for high- performance adsorption-photocatalysis[J]. Applied Clay Science, 2022, 218: 106427. [36] QIN M C, LIN X Y, GAN G Q, et al.Boosting electrocatalytic nitrogen fixation with Co-N3 site-decorated porous carbon[J]. ACS Sustainable Chemistry & Engineering, 2020, 8(35): 13430-13439. [37] MU J J, ZHAO Z W, GAO X W, et al.Bimetallic PdFe3 nano-alloy with tunable electron configuration for boosting electrochemical nitrogen fixation[J]. Advanced Energy Materials, 2024, 14: 2303558. [38] TANG Z C, ZHOU X Q, DU M Y, et al. Crystal plane regulation promotes the oriented conversion of radicals in heterogeneous persulfate catalyzed oxidation process[J/OL]. Nano Micro Small,[2024-04-10]. https://doi.org/10.1002/smll.202312173. [39] LUO L, ZHOU Y L, YAN W, et al.In-situ one-step synthesis of activated Carbon@MIL-101 (Cr) composites for hydrogen storage[J]. International Journal of Hydrogen Energy, 2022, 47(93): 39563-39571. [40] DUAN M J, GUAN Z Y, MA Y W, et al.A novel catalyst of MIL-101(Fe) doped with Co and Cu as persulfate activator: synthesis, characterization, and catalytic performance[J]. Chemical Papers, 2018, 72(1): 235-250. [41] ZHENG H N, SUN W J, CHEN Y, et al.Preparation and enhanced electrorheological properties of Ce-doped porous titanium oxide nanoparticles[J]. Industrial & Engineering Chemistry Research, 2021, 60(4): 1642-1655. [42] LI Q, ZHANG Y F, ZHANG M D, et al.Structural, electrical and magnetic properties of Gd-doped and (Al, Gd) codoped ZnO films[J]. Journal of Alloys and Compounds, 2023, 933: 167744. [43] FU J W, WANG L, CHEN Y H, et al.Enhancement of aqueous stability of NH2-MIL-101(Fe) by hydrophobic grafting post-synthetic modification[J]. Environmental Science and Pollution Research, 2021, 28(48): 68560-68571. [44] ZHANG J J, LIU R R, KUANG M, et al.Constructing CQDs/MIL-101(Fe)/g-C3N4 photocatalyst and its enhancement to the photocatalytic activity[J]. Materials Letters, 2023, 353: 135004. [45] GUO H S, GUO W L, LIU Y, et al.Quinone-modified metal-organic frameworks MIL-101(Fe) as heterogeneous catalysts of persulfate activation for degradation of aqueous organic pollutants[J]. Water Science and Technology, 2019, 79(12): 2357-2365. [46] TAKASHIMA T, FUKASAWA H, MOCHIDA T, et al.Cu-doped Fe2O3 nanorods for enhanced electrocatalytic nitrogen fixation to ammoni[J]. ACS Applied Nano Materials, 2023, 6(24): 23381-23389. [47] LUO S J, LI X M, GAO W G, et al.An MOF-derived C@NiO@Ni electrocatalyst for N2 conversion to NH3 in alkaline electrolytes[J]. Sustainable Energy Fuels, 2020, 4(1): 164-170. [48] QIN Q, ZHAO Y, SCHMALLEGGER M, et al.Enhanced electrocatalytic N2 reduction via partial anion substitution in titanium oxide-carbon composites[J]. Angewandte Chemie International Edition, 2019, 58(37): 13101-13106. [49] DUAN J J, SUN Y T, CHEN S, et al.A zero-dimensional nickel, iron-metal-organic framework (MOF) for synergistic N2 electrofixation[J]. Journal of Materials Chemistry A, 2020, 8(36): 18810-18815. [50] SONG P F, KANG L, WANG H, et al.Nitrogen (N), phosphorus (P)-codoped porous carbon as a metal-free electrocatalyst for N2 reduction under ambient conditions[J]. ACS Applied Materials Interfaces, 2019, 11(13): 12408-12414. [51] LIU P X, JING P Q, XU X, et al.Structural reconstruction of Ce-MOF with active sites for efficient electrocatalytic N2 reduction[J]. ACS Applied Engery Materials, 2021, 4(11): 12128-12136. [52] HE H M, ZHU Q Q, YAN Y, et al.Metal-organic framework supported Au nanoparticles with organosilicone coating for high-efficiency electrocatalytic N2 reduction to NH3[J]. Applied Catalysis B: Environmental, 2022, 302: 120840. [53] YUAN S, FENG L, WANG K C, et al.Stable Metal-organic frameworks: design, synthesis, and applications[J]. Advance Materials, 2018, 30(37): 1704303. [54] KHALI I E, XUE C, LIU W J, et al.The role of defects in metal-organic frameworks for nitrogen reduction reaction: when defects switch to features[J]. Advanced Functional Materials, 2021, 31(17): 2010052. [55] ZHU C Y, WEN C X, WANG C, et al.Elongated heterometal double-sites promote nitrogen reduction on two-dimensional MM'B7 monolayers[J]. Journal of Materials Chemistry A, 2021, 9(17): 10855-10868. [56] XIAO H, XIA M Y, CHONG B, et al.D-band center modulation of B-mediated FeS2 to activate molecular nitrogen for electrocatalytic ammonia synthesis[J]. Applied Catalysis B: Environmental, 2024, 343: 123474.