Effect of cryogenic rolling and aging heat treatment on microstructure and properties of Al-Zn-Mg aluminum alloy |
CHEN Songyi1,2,3, LIU Qiang1,3, CHEN Kanghua1,2,3, HUANG Lanping2 |
1. Light Alloy Research Institute, Central South University, Changsha 410083, China; 2. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China; 3. Collaborative Innovation Center of Advance Nonferrous Structural Materials and Manufacturing,Central South University, Changsha 410083, China |
|
|
Abstract The Al-Zn-Mg alloy sheets were aged by CR (cryogenic rolling)+480h natural aging, CR+100 ℃/12 h aging, CR+100 ℃/80 h aging and 100 ℃/107 h aging treatment for solution-quenched sheets without CR, respectively. The hardness and room temperature tensile properties of the alloys were determined,and exfoliation corrosion (EXCO) and electrochemical corrosion were carried out. The morphology and microstructure of Al-Zn-Mg alloys were observed by optical microscope, scanning electron microscope and transmission electron microscope. The effects of cryogenic rolling and different aging treatment (natural aging and different time artificial aging) on the micro-structure and properties of Al-Zn-Mg alloys were studied. The results show that the EXCO resistance and electrochemical corrosion resistance of CR+480 h natural aging and CR+100 ℃/12 h ageing treated alloys are worse than those of solution-quenched alloys treated directly at 100 ℃/107 h. The main reason is the formation of submicron, fibrous and high dislocation density ultrafine grains during cryogenic rolling. CR+100 ℃/80 h aging treatment alloy has better exfoliation corrosion resistance and electrochemical corrosion properties due to the formation of high density dislocations during cryogenic rolling, and coarse and discontinuous grain boundary precipitates are formed after subsequent 100 ℃/80 h aging treatment. In addition, the ultra-fine grain structure with high dislocation density was formed after cryogenic rolling, which significantly accelerated the aging hardening response.
|
Received: 04 September 2019
Published: 19 June 2020
|
|
|
|
|
[1] THOMPSON D S.Metallurgical factors affecting high strength aluminum alloy production[J]. Metall Mater Trans A, 1975, 6(4): 671-683. [2] HEIN A, HASZLER A, KEIDEL C, et al.Recent development in aluminum alloys for aerospace applications[J]. Materials Science & Engineering A, 2000, 280(1): 102-107. [3] 黄兰萍, 陈康华, 李松, 等. 高温预析出对Al-Zn-Mg合金板材应力腐蚀断裂的影响[J]. 稀有金属材料与工程, 2006, 35(12): 1943-1948. HUANG Lanping, CHEN Kanghua, LI Song, et al.Effect of high-temperature pre-precipitation on stress corrosion cracking of Al-Zn-Mg aluminum alloy[J]. Rare Metal Materials and Engineering, 2006, 35(12): 1943-1948. [4] PANIGRAHI S K, JAYAGANTHAN R.Effect of annealing on thermal stability, precipitate evolution, and mechanical properties of cryorolled Al7075 alloy[J]. Metallurgical & Materials Transactions A, 2011, 42(10): 3208-3217. [5] KRISHNA K G, SIVAPRASAD K, VENKATESWARLU K, et al.Microstructural evolution and aging behavior of cryorolled Al-4Zn-2Mg alloy[J]. Materials Science & Engineering A, 2012, 535(4): 129-135. [6] ZHAO Y H, LIAO X A, JIN Z, et al.Microstructures and mechanical properties of ultrafine grained 7075Al alloy processed by ECAP and their evolution during annealing[J]. Acta Materialia, 2004, 52(15): 4589-4599. [7] ZHAO Y H, LIAO X Z, ZHU Y T, et al.Enhanced mechanical properties in ultrafine grained 7075Al alloy[J]. Journal of Materials Research, 2005, 20(2): 288-291. [8] ZHAO Y H, LIAO X Z, CHENG S, et al.Simultaneously increasing the ductility and strength of nano-structured alloys[J]. Advanced Materials, 2010, 18(17): 2280-2283. [9] KRISHNA K G, SIVAPRASAD K, NARAYANAN T S N S, et al. Localized corrosion of an ultrafine grained Al-4Zn-2Mg alloy produced by cryorolling[J]. Corrosion Science, 2012, 60(1): 82-89. [10] KRISHNA K G, VENKATESWARLU K, KUMAR K C H. Tensile behavior of ultrafine-grained Al-4Zn-2Mg alloy produced by cryorolling[J]. Journal of Materials Engineering & Performance, 2011, 20(9): 1569-1574. [11] FERRAGUT R, POSITRON S A.Age-hardening and precipitation in predeformed 2024(Al-Cu-Mg) alloy[J]. Physica Status Solidi, 2015, 175(1): R1-R2. [12] 方家芳. 7A52铝合金组织与性能的研究[D]. 长沙: 中南大学, 2006. FANG Jiafang.Study on microstructure and properties of 7A52 aluminum alloy[D]. Changsha: Central South University, 2006. [13] 许晓静, 朱金鑫, 郭云飞, 等. 固溶-冷变形-时效工艺下超高强Al-Zn-Mg-Cu系铝合金的组织及性能[J]. 稀有金属材料与工程, 2017(10): 2981-2986. XU Xiaojing, ZHU Jinxin, GUO Yunfei, et al.Microstructures and properties of ultra-high utrength Al-Zn-Mg-Cu aluminum alloy under solution-cold deformation-aging[J]. Rare Metal Materials and Engineering, 2017(10): 2981-2986. [14] 彭国胜. 变形和热处理对Al-Zn-Mg-Cu系超强铝合金组织和性能的影响[D]. 长沙: 中南大学, 2012. PENG Guosheng.Effect of deformation and heat treatment on Microstructure and properties of Al-Zn-Mg-Cu superalloy[D]. Changsha: Central South University, 2012. [15] ZHANG Jianbo, ZHANG Yongan, HE Zhenbo, et al.Effect of natural aging on properties and microstructure of 7N01 aluminum alloys[J]. Chinese Journal of Rare Metals, 2012, 36(2): 191-195. [16] POSADA M, MURR L E, NIOU C S, et al.Exfoliation and related microstructures in 2024 aluminum body skins on aging aircraft[J]. Materials Characterization, 1997, 38(4/5): 259-272. [17] SONG D, MA A, JIANG J, LIN P, et al.Corrosion behavior of ultra-fine grained industrial pure Al fabricated by ECAP[J]. Trans Nonferr Metals Soc China, 2009, 19: 1065-1070. [18] DONG Chaofang, AN Yinghui, LI Xiaogang, et al.Electrochemical performance of initial corrosion of 7A04 aluminium alloy in marine atmosphere[J]. The Chinese Journal of Nonferrous Metals, 2009, 19(2): 346-352. [19] 孙擎擎, 孙睿吉, 陈送义, 等. 大气污染物对7B50 铝合金电化学腐蚀性能的影响[J]. 中国有色金属学报2015, 25(3): 575-581. SUN Qingqing, SUN Ruiji, CHEN Songyi, et al.Effect of atmospheric pollutants on electrochemical corrosion behaviour of 7B50 aluminium alloy[J]. The Chinese Journal of Nonferrous Metals, 2015, 25(3): 575-581. [20] 孙擎擎, 董朋轩, 孙睿吉, 等. 时效制度对挤压Al-6.2Zn- 2.3Mg-2.3Cu铝合金电化学腐蚀性能的影响[J]. 中国有色金属学报, 2015(4):866-874. SUN Qingqing, DONG Pengxuan, SUN Ruiji, et al.Effect of ageing process on electrochemical corrosion property of extruded Al-6.2Zn-2.3Mg-2.3Cu aluminium alloy[J]. The Chinese Journal of Nonferrous Metals, 2015(4): 866-874. [21] LUO P, MCDONALD D T, XU W, et al.A modified hall-petch relationship in ultrafine-grained titanium recyc [22] led from chips by equal channel angular pressing[J]. Scripta Materialia, 2012, 66(10): 785-788. [23] ROBINSON M J, JACKSON N C.The influence of grain structure and inter granular corrosion rate on exfoliation and stress corrosion cracking of high strength Al-Cu-Mg alloys[J]. Corrosion Science, 1999, 41(5): 1013-1028. [24] CHUNG M K, CHOI Y S, KIM J K, et al.Effect of the number of ECAP pass time on the electrochemical properties of 1050 Al alloys[J]. Mater Sci Eng A, 2004, 366: 282-291. [25] ABDULSTAAR M, MHAEDE M, WAGNER L, et al.Corrosion behaviour of Al 1050 severely deformed by rotary swaging[J]. Materials & Design, 2014, 57: 325-329. [26] XU X J, WANG C S, GUO Y F, et al.Effect of solid solution-cold deformation-prerecovery on microstructure and properties of Al-13.01Zn-3.16Mg-2.8Cu-0.204Zr-0.0757Sr aluminum alloy[J]. Transactions of Materials & Heat Treatment, 2017, 38(1): 37-42. |
|
|
|