粉末冶金材料科学与工程  2022, Vol. 27 Issue (6): 620-629    DOI: 10.19976/j.cnki.43-1448/TF.2022042
  工艺技术 本期目录 | 过刊浏览 | 高级检索 |
黑磷烯尺寸对黑磷烯/羟基磷灰石混合物气敏性能的影响
吴江松, 谭彦妮, 吕剑锋
中南大学 粉末冶金国家重点实验室,长沙 410083
Effect of size of black phosphorene on gas sensitivity of black phosphorene/hydroxyapatite hybrid
WU Jiangsong, TANYanni, LYU Jianfeng
State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China
全文: PDF (1300 KB)   HTML (0 KB) 
输出: BibTeX | EndNote (RIS)      
摘要 采用水热法制备短棒状羟基磷灰石(HA),通过液相剥离法制备黑磷烯(black phosphorene, BP),并采用不同的离心速率分离出具有不同尺寸的BP。制备BP质量分数为7.0%的BP/HA混合物,用X射线衍射仪、扫描电镜、透射电镜、原子力显微镜和拉曼光谱对混合物的物相组成、微观形貌和结构进行表征,同时使用气体传感系统研究纯HA以及含有不同尺寸BP的BP/HA混合物的气体传感特性。结果表明,加入BP可显著提高HA对氨气的响应,BP的尺寸越小,对HA气敏性能的提升越大。其中BP-10000/HA对浓度(气敏实验所用空气中氨气的体积分数)为100×10-6的氨气的响应高达58.7%,当氨气浓度上升到1 000×10-6后,响应高达98.3%。BP尺寸越小,气敏性能越好,可能是由于具有更大的比表面积,因而具备更多的活性位点。总之,BP可显著提升HA的气敏性能,BP/HA混合物是一种很有前途的室温气敏材料。
服务
把本文推荐给朋友
加入我的书架
加入引用管理器
E-mail Alert
RSS
作者相关文章
吴江松
谭彦妮
吕剑锋
关键词 羟基磷灰石黑磷烯(BP)室温氨气气敏    
Abstract:In this work, rod-shaped hydroxyapatite (HA) was prepared by hydrothermal method, and black phosphorene (BP) with different sizes was prepared by liquid-phase exfoliation and separated by adopting different centrifugation speed. BP/HA hybrid was prepared with BP at 7.0% mass fraction. The phase composition, micro-morphology and structure of BP/HA were characterized using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, atomic force microscopy and Raman spectroscopy. The gas sensing properties of pure HA and BP/HA with different sizes of BP were investigated using a gas sensing system. The results show that the addition of BP significantly improves the response of HA to ammonia, and the gas-sensing performance of HA is improved the most with the addition of BP with smaller size. Among them, the response of BP-10000/HA to the ammonia concentration of 100×10-6 is as high as 58.7%, and when the ammonia concentration isincreased to 1 000×10-6, the response is as high as 98.3%. The smaller the size of BP, the better the gas sensing performance may be due to its larger specific surface area and thus more active sites. In conclusion, BP can significantly improve the gas sensitivity of HA, and BP/HA is a promising gas sensitive material at room temperature.
Key wordshydroxyapatite    black phosphorene (BP)    room temperature    ammonia    gas sensing
收稿日期: 2022-03-18      出版日期: 2023-01-27
ZTFLH:  TQ174  
基金资助:湖南省自然科学基金青年基金项目(2019JJ50797)
通讯作者: 谭彦妮,副研究员,博士。电话:0731-88836296;E-mail: tanyanni@csu.edu.cn   
引用本文:   
吴江松, 谭彦妮, 吕剑锋. 黑磷烯尺寸对黑磷烯/羟基磷灰石混合物气敏性能的影响[J]. 粉末冶金材料科学与工程, 2022, 27(6): 620-629.
WU Jiangsong, TANYanni, LYU Jianfeng. Effect of size of black phosphorene on gas sensitivity of black phosphorene/hydroxyapatite hybrid. Materials Science and Engineering of Powder Metallurgy, 2022, 27(6): 620-629.
链接本文:  
http://pmbjb.csu.edu.cn/CN/10.19976/j.cnki.43-1448/TF.2022042     或     http://pmbjb.csu.edu.cn/CN/Y2022/V27/I6/620
版权所有 © 《粉末冶金材料科学与工程》编辑部
地址:长沙市麓山南路中南大学粉末冶金研究院 邮编:410083 电话:0731-88877163 邮箱:pmbjb@csu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn