Materials Science and Engineering of Powder Metallurgy  2021, Vol. 26 Issue (6): 547-553    DOI: 10.19976/j.cnki.43-1448/TF.2021044
Engineering and Technology Current Issue | Archive | Adv Search |
Microstructure and properties of new nickel-based superalloy powder prepared by argon atomization
NONG Bizhong, ZHANG Yazhou, LIU Zuming, WEI Bing, CAO Bin
State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China
Download: PDF (904 KB)   HTML (0 KB) 
Export: BibTeX | EndNote (RIS)      
Abstract  New nickel-based superalloy powder for selective laser melting with a total mass fraction of Al and Ti less than 4% was prepared by argon atomization. The composition, phase, morphology, microstructure and properties of the new nickel-based superalloy powder were characterized. The results show that the total mass fraction of Al and Ti in the new nickel-based superalloy powder was 3.82%. Small particle size powder (particle size<20 μm) has a compact interior structure, mainly cellular structure, and uniformly composition, and its micro-hardness (HV) reaches 265. As the particle size of the powder increases, the number of dendrites in the powder increases, and solidification shrinkage pore and particle-coating defect appear in some large-diameter (particle size>40 μm) powder. After sieving, the powder with a particle size of 15-44 μm has a concentrated particle size distribution, a median diameter DV50 of 19.7 μm, the flow- ability and apparent density are 15.14 s/50 g and 4.15 g/cm3, respectively.
Key wordsargon atomization      nickel-based superalloy      microstructure      powder properties      total content of Al and Ti     
Received: 31 March 2021      Published: 22 December 2021
ZTFLH:  TG146.1  
Service
E-mail this article
Add to my bookshelf
Add to citation manager
E-mail Alert
RSS
Articles by authors
NONG Bizhong
ZHANG Yazhou
LIU Zuming
WEI Bing
CAO Bin
Cite this article:   
NONG Bizhong,ZHANG Yazhou,LIU Zuming, et al. Microstructure and properties of new nickel-based superalloy powder prepared by argon atomization[J]. Materials Science and Engineering of Powder Metallurgy, 2021, 26(6): 547-553.
URL:  
http://pmbjb.csu.edu.cn/EN/10.19976/j.cnki.43-1448/TF.2021044     OR     http://pmbjb.csu.edu.cn/EN/Y2021/V26/I6/547
Copyright © Editorial Board of Materials Science and Engineering of Powder Metallurgy
Tel: 0731-88877163 E-mail: pmbjb@csu.edu.cn
Supported by: Beijing Magtech