Effect of TiO2 content on properties of loess ceramic membrane support
SHEN Zao1, ZHOU Guangrui2, TONG Zhi2, WANG Jiayue2, YAN Xiao2
1. Xi’an Zhonghe City Engineering Supervision Consulting Co., Ltd, Xi’an 710048, China;
2. School of Environmental and Chemical Engineering, Xi’an Polytechnic University, Xi’an 710048, China
Abstract Taking Luochuan loess with an average particle size of 38.78 μm as the aggregate, lignocellulosic (LCS) as pore former and binder, titanium dioxide (TiO2) as the sintering assistant, the rolling molding method was used to prepare the tubular porous loess ceramic support, which were characterized by pure water flux, flexural strength, acid/alkali resistance, analysis of crystal phase composition and observation of surface morphology. The effects of TiO2 content on the properties of the ceramic membrane support were investigated. The results show that the addition of TiO2 can promote the sintering and densification of loess ceramic membrane support. When the sintering temperature is 1 050 ℃ and TiO2 content is 4%, the flexural strength is 31.97 MPa, the pure water flux is 3 487.27 L/(m2·h·MPa), the porosity is 33.48%, the average pore size is 3.14 μm, the mass loss rate of acid/alkali corrosion is only 0.14% and 0.13%, and the surface of the support has a uniform grain size and more micropores.
SHEN Zao,ZHOU Guangrui,TONG Zhi, et al. Effect of TiO2 content on properties of loess ceramic membrane support[J]. Materials Science and Engineering of Powder Metallurgy, 2019, 24(5): 485-490.
[1] ISSAOUI M, BOUAZIZ J, FOURATI M.Elaboration of membrane ceramic supports using aluminum powder[J]. Desalination & Water Treatment, 2015, 53(4): 1037-1044. [2] LI L, CHEN M, DONG Y, et al.A low-cost alumina-mullite composite hollow fiber ceramic membrane fabricated via phase-inversion and sintering method[J]. Journal of the European Ceramic Society, 2018, 36(8): 2057-2066. [3] MANSOUR I, LIONEL L, LEBEAU B, et al.Design and characterization of flat membrane supports elaborated from kaolin and aluminum powders[J]. Comptes Rendus-Chimie, 2016, 19(4): 496-504. [4] KOK K N, CHENG-F L, SRI C P, et al.Reduced membrane fouling in novel bio-entrapped membrane reactor for treatment of food and beverage processing wastewater[J]. Water Research, 2011, 45: 4269-4278. [5] 伍海东, 刘伟, 伍尚华, 等. 陶瓷增材制造技术研究进展[J]. 陶瓷学报, 2017, 8(4): 451-458. WU Haidong, LIU Wei, WU Shanghua, et al.Research progress of additive manufacturing technology for ceramic materials[J]. Journal of Ceramics, 2017, 8(4): 451-458. [6] 吴懋亮, 孙翰霆, 刘中俊, 等. 烧结助剂对氧化铝陶瓷低温烧结的影响[J]. 上海电力学院学报, 2019, 35(1): 11-15. WU Maoliang, SUN Hanting, LIU Zhongjun, et al.Influence of sintering additive on low temperature sintering process of Al2O3 ceramics[J]. Journal of Shanghai University of Electric Power, 2019, 35(1): 11-15. [7] 陈仕俊, 余阳, 林晓亮, 等. 低温烧结制备氧化铝陶瓷膜支撑体[J]. 人工晶体学报, 2017, 46(5): 825-831. CHEN Shijun, YU Yang, LIN Xiaoliang, et al.Preparation of alumina ceramic membrane support at low sintering temperature[J]. Journal of Synthetic Crystals, 2017, 46(5): 825-831. [8] 漆虹, 邢卫红, 范益群. 低温烧成高纯Al2O3多孔陶瓷膜支撑体的制备[J]. 硅酸盐学报, 2010, 38(2): 283-288. QI Hong, XING Weihong, FAN Yiqun.Preparation of high purity alumian macroporous support at low sintering temperature[J]. Journal of the Chinese Ceramic Society, 2010, 38(2): 283-288. [9] BOSE S, DAS C.Preparation and characterization of low cost tubular ceramic support membranes using sawdust as a pore- farmer[J]. Materials letters, 2013, 110(1): 152-155. [10] 王焕平, 张斌, 马红萍, 等. CuO-TiO2复合助剂低温烧结氧化铝陶瓷的机理(Ⅱ)[J]. 材料研究学报, 2010, 24(1): 37-43. WANG Huanping, ZHANG Bin, MA Hongping, et al.Mechanism of lowering the sintering temperature of Al2O3 ceramic by the addition of CuO-TiO2(Ⅱ)[J]. Chinese Journal of Materials Research, 2010, 24(1): 37-43. [11] 胡继林, 刘鑫, 曹宇, 等. MnO2-TiO2-CaO-La2O3复相添加剂对低温烧结氧化铝陶瓷性能的影响[J]. 中国陶瓷, 2011, 32(4): 548-551. HU Jiling, LIUXin, CAO Yu, et al.Influences of MnO2-TiO2- CaO-La2O3 composite additives on properties of alumina ceramics prepared by low-temperature sintering[J]. Journal of Ceramics, 2011, 32(4): 548-551. [12] GB/ T2833—1996, 陶管弯曲强度试验方法[S]. 北京: 中国标准出版社, 1996. GB/T 2833—1996, Test method for flexural strength[S]B/T 2833—1996, Test method for flexural strength[S]. Beijing: China Standard Press, 1996. [13] GB/T 1970—1996, 多孔陶瓷耐酸、碱腐蚀性能试验方法[S]B/T 1970—1996, 多孔陶瓷耐酸、碱腐蚀性能试验方法[S].北京: 中国标准出版社, 1996. GB/T 1970—1996, Test method for acid and alkali corrosion resistance of porous ceramics[S]B/T 1970—1996, Test method for acid and alkali corrosion resistance of porous ceramics[S]. Beijing: China Standard press, 1996. [14] YANG Y, HAN F, XU W, et al.Low-temperature sintering of porous silicon carbide ceramic support with SDBS as sintering aid[J]. Ceramics International, 2016, 43(3): 3377-3383. [15] R J B.Effrct of TiO2 on initial sintering of Al2O3[J]. Journal of the American Ceramic Society, 1972, 55(2): 114-115. [16] 周世界, 蒋晓曙, 左李萍, 等. 云母-透辉石可加工复合材料的制备[J]. 中国陶瓷, 2013, 49(3): 41-43. ZHOU Shijie, JIANG Xiaoshu, ZUO Liping, et al.Preparation of mica diopside workable com posite-material[J]. Journal of Ceramics, 2013, 49(3): 41-43. [17] IVAN B C, E RW. Solid solution of TiO2 in Al2O3[J]. Journal of the American Ceramic Society, 1966, 49(12): 634-637. [18] 陈安康, 同帜, 王丹, 等. 以TiO2-MgO-MnO2为烧结助剂挤压成形低温烧结α-Al2O3陶瓷膜支撑体[J]. 陶瓷, 2017(5): 13-18. CHEN Ankang, TONG Zhi, WANG Dan, et al.Low temperature sintering of alumina ceramic support with TiO2-MgO-MnO2 multiphase sintering additive[J]. Ceramics, 2017(5): 13-18. [19] H M, S M A, A Z A.A, Effects of TiO2 addition on the phase, mechanical properties, and microstructure of zirconia-toughened alumina ceramic composite[J]. Ceramics International, 2015, 41(3): 3961-3967. [20] H Q, Y Q F.Effect of TiO2 doping on the characteristics of macroporous Al2O3/TiO2 membrane supports[J]. Journal of the European Ceramic Society, 2010, 30(6): 1317-1325. [21] 同帜, 刘婷, 王丹, 等. 烧结温度对氧化铝陶瓷膜支撑体性能的影响[J]. 化学工程, 2018, 46(12): 15-20. TONG Zhi, LIU Ting, WANG Dan, et al.Effect of sintering temperature on properties of alumina ceramic supports in complex sintering[J]. Chemical Engineering (China), 2018, 46(12): 15-20.
2019, Vol. 24 