Materials Science and Engineering of Powder Metallurgy  2018, Vol. 23 Issue (6): 614-618    DOI:
Engineering and Technology Current Issue | Archive | Adv Search |
Effects of particle size and dispersion of TiC on the microstructure and tensile strength of Mo alloy
CHEN Jiyong, FAN Jinlian, CHENG Huichao
Powder Metallurgy Research Institute, Central South University, Changsha 410083, China
Download: PDF (357 KB)   HTML (0 KB) 
Export: BibTeX | EndNote (RIS)      
Abstract  Two Mo-TiC alloys with TiC mass fraction of 6% were prepared by powder metallurgy using ultrafine TiC powder with a particle size of 0.5 μm and a nanometer TiC powder with a particle size of 0.05 μm as raw materials. The effects of particle size and dispersion of TiC on the microstructures and tensile strength of Mo-TiC alloys were studied. The results show that, compared to the addition of ultrafine TiC powder, the addition of nanometer TiC powder has a significant improvement on the tensile strength of the alloy, but because the agglomeration of nano TiC powder in the matrix. When sintered at 1 950 ℃, the tensile strength of Mo-nano TiC alloy reaches 515 MPa, which is more than 30% higher than that of Moultrafine TiC alloy. After adding organic compound as a dispersant, the TiC aggregates in the Mo base are transformed from the spheroid to elongated shape, and some of the nanoscale TiC are fully dispersed the alloy grain is further refined and the strength of the alloy is improved. The tensile strength of the material sintered at 1 850 ℃ reaches 615 MPa.
Key wordsMo-TiC alloy      TiC granularity      agglomeration      organic dispersant      tensile strength     
Received: 28 March 2018      Published: 19 July 2019
ZTFLH:  TG146.412  
Service
E-mail this article
Add to my bookshelf
Add to citation manager
E-mail Alert
RSS
Articles by authors
CHEN Jiyong
FAN Jinlian
CHENG Huichao
Cite this article:   
CHEN Jiyong,FAN Jinlian,CHENG Huichao. Effects of particle size and dispersion of TiC on the microstructure and tensile strength of Mo alloy[J]. Materials Science and Engineering of Powder Metallurgy, 2018, 23(6): 614-618.
URL:  
http://pmbjb.csu.edu.cn/EN/     OR     http://pmbjb.csu.edu.cn/EN/Y2018/V23/I6/614
Copyright © Editorial Board of Materials Science and Engineering of Powder Metallurgy
Tel: 0731-88877163 E-mail: pmbjb@csu.edu.cn
Supported by: Beijing Magtech