Materials Science and Engineering of Powder Metallurgy  2018, Vol. 23 Issue (4): 361-367    DOI:
Engineering and Technology Current Issue | Archive | Adv Search |
Fabrication and mechanical properties of porous Ni wicks
LI Qiang, GAN Xueping, LI Zhiyou, ZHOU Kechao
State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China
Download: PDF (0 KB)   HTML (0 KB) 
Export: BibTeX | EndNote (RIS)      
Abstract  Porous Ni wicks with high porosity and controllable pore characteristics were fabricated by powder metallurgy method using polymethylmethacrylate (PMMA) as pore-forming agent and carbonyl Ni powder as raw material. The phase composition, micro-structure and mechanical properties of porous Ni were investigated by X-ray diffraction (XRD), scanning electron microscope SEM and mechanical testing instrument. The effects of sintering temperature, the particle size and content of PMMA on pore structures and mechanical properties of porous Ni were investigated. The results show that with the increase of sintering temperature, the porosity and average pore size decrease, mechanical properties increase. With the increase of the particle size and content of PMMA, the porosity and average pore size increase, mechanical properties decrease. The porous Ni wicks with the most excellent comprehensive performance can be fabricated by sintering at the temperature of 800 ℃ with 80% volume fraction addition of PMMA (5 μm). The porosity, average pore size, flexural strength and compressive strength are 71.9%, 2.37 μm, 25.3 MPa and 8.7 MPa, respectively.
Key wordsporous Ni      sintering temperature pore-forming agent      porosity      mechanical properties     
Received: 06 December 2017      Published: 12 July 2019
ZTFLH:  TG146.1+5  
Service
E-mail this article
Add to my bookshelf
Add to citation manager
E-mail Alert
RSS
Articles by authors
LI Qiang
GAN Xueping
LI Zhiyou
ZHOU Kechao
Cite this article:   
LI Qiang,GAN Xueping,LI Zhiyou, et al. Fabrication and mechanical properties of porous Ni wicks[J]. Materials Science and Engineering of Powder Metallurgy, 2018, 23(4): 361-367.
URL:  
http://pmbjb.csu.edu.cn/EN/     OR     http://pmbjb.csu.edu.cn/EN/Y2018/V23/I4/361
Copyright © Editorial Board of Materials Science and Engineering of Powder Metallurgy
Tel: 0731-88877163 E-mail: pmbjb@csu.edu.cn
Supported by: Beijing Magtech