Microstructure control and grain refinement mechanism of ceramic corundum abrasives prepared by sol-gel combined with two step sintering process
ZHAO Jiong1, LI Zhuan1, ZOU Lingfeng2, TANG Huixian1, XU Yang1, LI Yuxing1, ZOU Huijing3
1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China; 2. College of Materials Science and Engineering, Changsha University of Science and Technology, Changsha 410114, China; 3. College of Arts and Science, New York University, New York 10012, United States
Abstract:Ceramic corundum abrasive precursor containing La2O3-TiO2-SiO2 composite additive was prepared by sol-gel method using pseudo boehmite with grain diameter of 6 μm as raw material. The ceramic corundum abrasives were prepared by conventional sintering method and two-step sintering method, respectively. The microstructure and element distribution of abrasives were analyzed by SEM and TEM, and the grain sizes were analyzed by imagePro software. The results show that the temperature of the first sintering stage significantly affects the final grain size of the abrasive when the two-step sintering method is adopted. Due to the low temperature in the second sintering stage, the later sintering mechanism changes from grain boundary migration to grain boundary diffusion, thus the grains are significantly refined and the abnormal grain grow this avoided. Appropriately reducing the sintering temperature in the second stage is conducive to obtaining fine equiaxed grains with uniform distribution, but it will lead to a decrease in abrasive density. Compared with the corundum abrasives prepared by the traditional sintering method, the abrasives prepared by the two-step sintering method have a smaller grain size, uniform size and high hardness, although the density is reduced. Fine and uniform equiaxed grains are obtained by two-step sintering at 1 300 ℃ and 1 200 ℃ for 10 h, respectively. The average grain size is (334±97) nm, and the density and hardness (HV) are 3.87 g/cm3 and (18.3±0.29) GPa, respectively.
赵炯, 李专, 邹凌峰, 唐惠娴, 许阳, 李郁兴, 邹慧璟. 溶胶-凝胶法结合二步烧结制备陶瓷刚玉磨料的微结构控制及晶粒细化机理[J]. 粉末冶金材料科学与工程, 2022, 27(3): 319-326.
ZHAO Jiong, LI Zhuan, ZOU Lingfeng, TANG Huixian, XU Yang, LI Yuxing, ZOU Huijing. Microstructure control and grain refinement mechanism of ceramic corundum abrasives prepared by sol-gel combined with two step sintering process. Materials Science and Engineering of Powder Metallurgy, 2022, 27(3): 319-326.
[1] 李子成. 纳米晶陶瓷刚玉磨料的制备及性能研究[D]. 天津:天津大学, 2009. LI Zicheng.Preparation and performance of nanocrystalline corundum abrasive[D]. Tianjin: Tianjin University, 2009. [2] LUO M D, LI Z C, ZHU Y M.Effect of CuO-TiO2-SiO2 additions on the sintering behavior and mechanical properties of corundum abrasive synthesized through sol-gel method[J]. Ceramic International, 2013, 39(2): 1827-1833. [3] CHANG S, DOREMUS R H.Hot-pressing of nano-size alumina powder and the resulting mechanical properties[J]. International Journal of Applied Ceramic Technology, 2004, 1(2): 172-179. [4] CHENG J, AGRAWAL D.Microwave sintering of transparent alumina[J]. Materials Letters, 2002, 56(4): 587-592. [5] RIVERO-ANTÚNEZ P, CANO-CRESPO R, SÁNCHEZ-BAJO F. Reactive SPS for sol-gel alumina samples: structure, sintering behavior, and mechanical properties[J]. Journal of the European Ceramic Society, 2021, 41(11): 5548-5557. [6] YOU Z, KIYOSHI H, YUKIHIKO Y, et al.Densification and grain growth in pulse electric current sintering of alumina[J]. Journal of the European Ceramic Society, 2004(24): 3465-3470. [7] CHEN I W, WANG X H.Sintering dense nanocrystalline ceramics without final-stage grain growth[J]. Nature, 2000, 404(6774): 168-171. [8] LI Z C, LI Z H, ZHANG A J, et al. Synthesis processes of nano alumina abrasive[J]. Key Engineering Materials, 2008, 368/372(p.p): 691-693. [9] LI J G, YE Y P, SHEN L Y, et al.Densification and grain growth during pressureless sintering of TiO2 nanoceramics[J]. Materials Science and Engineering A, 2005, 390(1/2): 265-270. [10] GRECZYNSKI G, HULTMAN L.X-ray photoelectron spectroscopy: towards reliable binding energy referencing[J]. Progress in Materials Science, 2019, 107: 100591. [11] YANG J K, KIM W S, PARK H H.Chemical bonding states and energy band gap of SiO2-incorporated La2O3 films on n-GaAs (001)[J]. Thin Solid Films, 2006, 494(1): 311-314. [12] PISKUA Z S, STODOLNY M, GABAA E.Application of SiO2-La2O3 amorphous mesoporous nanocomposites obtained by modified sol-gel method in high temperature catalytic reactions[J]. Journal of Alloys and Compounds, 2020, 840: 155635. [13] LI L, ZENG F H, LI W J, et al.Nitrogen absorption behavior and mechanism of TiZrMnFe getter alloy[J]. Vacuum, 2020, 183: 109814. [14] WANG S H, WEI W, GAO Y H, et al.Characterization of Ti-Zr-V thin films deposited by DC and unipolar pulsed DC magnetron sputtering[J]. Vacuum, 2021, 188: 110200. [15] BODIOVÁ K, AJGALÍK P, GALUSEK D, et al. Two-stage sintering of alumina with submicrometer grain size[J]. Journal of the American Ceramic Society, 2007, 90(1): 3465-3470. [16] ZHOU M, HUANG Z Y, QI J Q, et al.Densification and grain growth of Al2O3 nanoceramics during pressureless sintering[J]. Journal of the American Ceramic Society, 2010, 89(1): 139-143. [17] LAGO O C, ADRIANA F J, ANDRÉ D, et al.Mechanical characterisation and hydrothermal degradation of Al2O3-15vol% ZrO2 nanocomposites consolidated by two-step sintering[J]. Ceramic International, 2018, 44(14): 16128-16136. [18] 胡赓祥, 蔡珣, 戎咏华. 材料科学基础[M]. 上海: 上海交通大学出版社, 2010: 195-232. HU Gengxiang, CAI Xun, RONG Yonghua.Fundamentals of Materials Science[M]. Shanghai: Shanghai Jiao Tong University Press, 2010: 195-232. [19] LIU J L, WANG Y G, YANG F Q, et al.Grain refining in spark plasma sintering Al2O3 ceramics[J]. Journal of Alloys & Compounds, 2015, 622(15): 596-600. [20] OJAIMI C L, FERREIRA J A, SANTOS F A, et al.Mechanical characterisation and hydrothermal degradation of Al2O-15vol% ZrO2 nanocomposites consolidated by two-step sintering[J]. Ceramics International, 2018, 44(14): 16128-16136. [21] 毛暄. 不同尺寸α-Αl2O3纳米颗粒的烧结特性研究[D]. 兰州:兰州大学, 2014. MAO Xuan.Sintering behavior study of α-Αl2O3 nanoparticles with different sizes[D]. Lanzhou: Lanzhou University, 2014. [22] 李文学. 陶瓷刚玉磨料的制备工艺及其性能研究[D]. 天津:天津大学, 2007. LI Wenxue.Study on preparation process and properties of ceramic corundum abrasives[D]. Tianjin: Tianjin University, 2007. [23] COBLE R L.Initial sintering of alumina and hematite[J]. Journal of the American Ceramic Society, 2006, 41(2): 55-62. [24] KINGERY W D, BERG M.Study of the initial stages of sintering by viscous flow, evaporation—condensation, and self- diffusion[J]. Journal of Applied Physics, 1990, 26(10): 367-382.