HfC添加对钼钨合金高温等离子烧蚀性能影响及机理分析

Abstract
Figure/Table
References
Related Citation (7)

Download: PDF (812 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The plasma ablation system combined with scanning electron microscopy (SEM) in this work were used to investigate the effects of different amounts of HfC particles on ablation performance and ablation morphology of sintered and rolled molybdenum-tungsten (Mo-W) alloys. Also, the high temperature ablation mechanism of the alloys was further discussed. The results show that the addition of HfC can significantly improve the ablation resistance of the alloys, including sintered and rolled alloys. The ablation resistance of the rolled alloys is obviously better than that of the sintered alloys due to the formation of lamellar structure and eliminating the internal defects (such as pores and impurity) after the rolled treatment. Compared with oxyacetylene ablation experiment, the plasma ablation experiment has protective gas along with strong impact force during ablation process. The ablation process is mainly physical and mechanical ablation. HfC doping mechanism is mainly because of its high melting point as a stagnation point. On the other hand, a small amount of HfO₂ film formed on the substrate also has protection effect. As a result, high temperature ablation property of Mo-W alloys is increased.

Key words： Mo-W alloy HfC plasmas ablation ablation mechanism and models ablation resistance

Received: 05 November 2017 Published: 12 July 2019

ZTFLH:

TG174.4

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YANG Lilin
	ZHANG Qifu
	HE Zhiyong
	LI Xiaogang

Cite this article:

YANG Lilin,ZHANG Qifu,HE Zhiyong, et al. Effects of HfC addition on plasma flame flow ablation resistance of molybdenum-tungsten alloys and its mechanism analysis[J]. Materials Science and Engineering of Powder Metallurgy, 2018, 23(2): 137-146.

URL:

http://pmbjb.csu.edu.cn/EN/ OR http://pmbjb.csu.edu.cn/EN/Y2018/V23/I2/137

[1] 郭磊, 宋瑞, 淡新国, 等. 稀土钼合金制备工艺及强韧化机理研究现状[J]. 中国钼业, 2017, 41(2): 45-51.
GUO Lei, SONG Rui, DAN Xinguo, et al.Present research status of preparation technology of rare Earth molybdenum- alloys and strengthening-toughening mechanism[J]. China Molybdenum Industry, 2017, 41(2): 45-51.
[2] 董帝, 王承阳. 钼合金制备工艺的研究进展[J]. 粉末冶金技术, 2017, 35(4): 304-309.
DONG Di, WANG Chengyang.Research progress on preparation technology of molybdenum alloy[J]. Powder Metallurgy Technology, 2017, 35(4): 304-309.
[3] 张盘龙, 倪锋, 赵晶晶, 等. 钼基掺杂合金的研究现状[J]. 硬质合金, 2013, 30(2): 107-112.
ZHANG Panlong, NI Feng, ZHAO Jingjing, et al.Research status of doped molybdenum-based alloys[J]. Cemented Carbide, 2013, 30(2): 107-112.
[4] 李鹏飞, 成会朝, 范景莲, 等. 热分解碳对注射成形钼合金性能和显微组织的影响[J]. 粉末冶金材料科学与工程, 2011, 16(1): 86-89.
LI Pengfei, CHENG Huichao, FAN Jinglian, et al.Effect of thermal decomposed carbon on properties and microstructures of molybdenum alloys prepared by powder injection molding[J]. Materials Science and Engineering of Powder Metallurgy, 2011, 16(1): 86-89.
[5] 何斌衡, 杨海林, 阮建明. Y₂O₃含量对钼合金组织和性能的影响[J]. 粉末冶金材料科学与工程, 2012, 17(2): 234-239.
HE Binheng, YANG Hailin, RUAN Jianming.Effect of Y₂O₃ content on microstructure and properties of molybdenum alloys[J]. Materials Science and Engineering of Powder Metallurgy, 2012, 17(2): 234-239.
[6] 李治斌, 涂鹤龄, 吴奉生. 85W-15Mo钨钼合金切削工艺[J]. 航天制造技术, 1989, 7(2): 11-15.
LI Zhibin, TU Heling, WU Fengsheng.85W-15Mo tungsten and molybdenum alloy cutting process[J]. Aerospace Manufacturing Technology, 1989, 7(2): 11-15.
[7] WANG Y J, LI H J, FU Q G, et al.Ablation behaviour of a TaC coating on SiC coated C/C composites at different temperatures[J]. Ceramics International, 2013, 39(1): 359-365.
[8] CHEN S, ZHANG C, ZHANG Y, et al.Mechanism of ablation of 3D C/ZrC-SiC composite under an oxyacetylene flame[J]. Corrosion Science, 2013, 68(1): 168-175.
[9] LI C, LI K, LI H, et al.Mechanical and thermophysical properties of carbon/carbon composites with hafnium carbide[J]. Ceramics International, 2013, 39(6): 6769-6776.
[10] CHAKRABORTY S P, BANERJEE S, SANYAL G, et al.Studies on the synthesis of Mo-30wt.%W alloy by non-conventional approaches[J]. Journal of Alloys and Compounds, 2010, 501(2): 211-217.
[11] SONG G M, ZHOU Y, WANG Y J.Effect of carbide particles on the ablation properties of tungsten composites[J]. Materials Characterization, 2003, 50(4): 293-303.
[12] PATRA A, SAXENA R, KARAK S K.Combined effect of Ni and nano-Y₂O₃ addition on microstructure, mechanical and high temperature behavior of mechanically alloyed W-Mo[J]. International Journal of Refractory Metals and Hard Materials, 2016, 60: 131-146.
[13] LEE D, UMER M A, RYU H J, et al.Elevated temperature ablation resistance of HfC particle-reinforced tungsten composites[J]. International Journal of Refractory Metals and Hard Materials, 2014, 43(12): 89-93.
[14] 成会朝, 范景莲, 李鹏飞, 等. 难熔钼合金的高温抗氧化和烧蚀行为[J]. 中国有色金属学报, 2011, 21(3): 570-576.
CHEN Huichao, FAN Jinglian, LI Pengfei, et al.Oxidation resistance and ablation behavior of refractory Mo alloy at high temperature[J]. The Chinese Journal of Nonferrous Metals, 2011, 21(3): 570-576.
[15] QUSAI M. MISTARIHI, VIVEK R, JOON HUI KIM, HO JIN RYU.Thermal conductivity of Mo-reinforced ZrO₂ composites fabricated by spark plasma sintering for inert matrix fuels[J]. Materials and Design, 2017, 134: 476-485.
[16] 张国君, 孙院军, 牛荣梅, 等. 稀土氧化镧掺杂钼合金的强化机制研究[J]. 稀有金属材料科学与工程, 2005, 34(12): 1926-1929.
ZHANG Guojun, SUN Yuanjun, NIU Rongmei, et al.The strengthening mechanism of rare earth lanthanum oxide doped molybdenum alloys[J]. Rare Metal Materials and Engineering, 2005, 34(12): 1926-1929.
[17] 曾建辉. 稀土金属冶炼用新型钨钼材料的研制[J]. 稀土, 1999, 20(5): 19-21.
ZENG Jianhui.Development of new tungsten and molybdenum materials for refining of rare earth metals[J]. Chinese Rare Earths, 1999, 20(5): 19-21.
[18] YANG Lilin, ZHANG Qifu, HE Zhiyong, et al.Influences of HfC particles on microstructure, mechanical properties and ablation resistance at elevated temperature of Mo-15W-HfC alloys[J]. International Journal of Refractory Metals and Hard Materials, 2017, 67: 56-67.
[19] 孟祥艳, 刘运传, 王康, 等. 酚醛树脂基复合材料的等离子烧蚀性能[J]. 材料科学与工程学报, 2016, 34(3): 400-403.
MENG Xiangyang, LIU Yunchuan, WANG Kang, et al.Plasma arc ablation behavior of phenolic resin based composites[J]. Journal of Materials Science and Engineering, 2016, 34(3): 400-403.
[20] 葛毅成, 彭可, 杨琳, 等. C/C-Cu复合材料表面等离子喷涂钨涂层[J]. 粉末冶金材料科学与工程, 2010, 15(2): 136-140.
GE YiCheng, PENG Ke, YANG Lin, et al.Coating tungsten on C/C-Cu composites surface by plasma spraying[J]. Materials Science and Engineering of Powder Metallurgy, 2010, 15(2): 136-140.
[21] 薛亮, 苏哲安, 杨鑫, 等. 先驱体浸渍裂解法制备三维C/C- HfC复合材料及其烧蚀性能[J]. 新型炭材料, 2017, 32(3): 265-270.
XUE Liang, SU Zhean, YANG Xin, et al.Ablation behavior of a three-dimensional C/C-HfC composite prepared by a precursor infiltration and pyrolysis method[J]. New Carbon Materials, 2017, 32(3): 265-270.